Intergranular corrosion of a light aircraft aluminum alloy propeller

Examination of the wreckage of a light aircraft revealed that approximately 20 cm was missing from one tip of the aluminum alloy propeller. Fractographic and metallographic examination of the remaining portion of the propeller revealed extensive grain-boundary separation in the vicinity of the fracture, and grain edges and corners rounded by corrosion on the fracture surface. Energy dispersive X-ray analysis (EDXA) revealed fluorine on, and in the vicinity of, the fracture surface. In the ensuing litigation, it was asserted that the crash occurred because the propeller fractured in flight as the result of intergranular attack caused by the use of a fluorine-bearing cleaner.     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

半固态ZnAl 27合金及其二次加热组织

研究了半固态ZnAl27合金及其二次加热组织。结果表明，半固态ZnAl27合金基本无宏观偏析，其组织为细小均匀的近球形非枝晶，综合力学性能远远高于常规铸造合金；二次加热后，α相进一步球化，边缘变得光滑圆整，可以满足半固态触变成形的需要。     

激光熔覆Ni基SiC合金涂层组织与性能的研究

利用5kWCO2连续波激光器在16Mn钢基材表面对含20%(体积比)SiC陶瓷粉末的镍基自熔性合金粉末进行激光熔覆得到Ni基SiC合金涂层(NiSiC)。研究了合金涂层的组织形貌及相结构,并用单纯的镍基合金涂层(Ni60)进行了显微硬度及滑动磨损性能的对比试验。结果表明,NiSiC合金涂层由γ枝晶及其间的共晶组织组成,主要组成相为γ-Ni,γ-(Ni,Fe)固溶体和(Cr,Fe)7C3,Cr23C6及(Cr,Si)3Ni3Si等化合物。添加SiC的镍基合金涂层NiSiC比单纯的镍基合金涂层Ni60具有较高的硬度和耐磨性。     

化学镀非晶态Ni—B合金的研究

本文通过化学镀方法在铜和钢上沉积非晶态Ni-B合金。着重讨论了还原剂浓度、络合剂浓度对化学镀沉积速率的影响;分析了它的耐蚀原因和其显微硬度随退火温度的变化情况并就其应用和发展略作说明。     

钨合金圆筒爆破试验破片分布的统计分析

采用圆筒爆破试验方法研究了易碎型钨合金的破片分布特征,并与93W合金的结果进行了对比.对破片的数量和质量分布特征进行了统计分析,发现易碎型钨合金的破片率明显高于93W合金,而且破片的均匀性也明显好于93W合金,但易碎钨合金的破片回收率低于93W合金,而且受装药量的影响较大.     

微晶合金在电流互感器中的应用

从微晶合金的性能特点出发，分析了其在电流互感器中的应用前景。     

45钢表面超音速电弧喷涂Ti-Al涂层的组织与性能研究

采用自行开发研制的超音速电弧喷设备，在45钢表面制成了钛铝合金复合涂层。并利用金相显微镜、X射线衍射仪、扫描电镜、电子探针，对涂层的成分、相结构、显微组织及其结合强度、显微硬度进行了研究。结果表明，利用超音速电弧喷涂设备，可以在45钢表面形成 度高、孔隙率低，结合强度较好和硬度高的Ti-Al合金涂层。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

MoSi2发热体在熔铝炉中的运用

以电阻熔铝炉技术改造实践为例，介绍一种高效、节能、不渗铁的新型熔铝炉——二硅化钼熔铝炉的设计。